13. Effect of Annealing Process on the Microstructures and Mechanical Properties of AZ31B/A356 Composite Plate Fabricated by Cast Rolling
The effect of annealing process on the microstructures and mechanical properties of Mg/Al composite plates fabricated by cast-rolling was investigated in this study. The results show that the interfacial transition zone can be divided into three regions: a Mg transition region, an Al transition region, and an intermediate region, respectively. The microhardn
Mat. Res.. Publicado em: 10/07/2019
-
14. Study of Mechanical Behavior and X-Ray Elastic Constants of Nickel Alloy Weld Overlay
The study of nickel-based alloy 625 clad (weld overlay) by X-ray diffraction (XRD) is difficult and often impossible because of its coarse and anisotropic microstructure. In this work, a sample preparation including machining, grinding, and annealing was proposed to avoid this negative effect in XRD analysis. Electron backscatter diffraction and hardness tes
Mat. Res.. Publicado em: 10/07/2019
-
15. Esculent coating of spider silk enhanced the preservation and shelf life of apricot
Resumo Segundo a Organização para Alimentação e Agricultura (FAO), cerca de um terço do total de alimentos produzidos é perdido globalmente. A principal causa deste desperdício é a perecibilidade das frutas e legumes. Portanto, os pesquisadores têm se esforçado para desenvolver uma técnica de preservação eficaz. Nosso estudo explorou a potencial
Braz. J. Biol.. Publicado em: 04/07/2019
-
16. Softening Behavior During Annealing of Overaged and Cold-rolled Aluminum Alloy 7075
This work proposes studying the softening kinetics of aluminum alloy 7075-T6. Firstly, AA 7075 strips were overaged (300°C and 5 hours). Then, the overaged strips were cold-rolled at room temperature (45% in thickness reduction) and, after that, annealed at different temperatures (200°C and 250°C) and time intervals (30 minutes - 4 hours). By using polari
Mat. Res.. Publicado em: 30/05/2019
-
17. Crystallization Behavior and Mechanical Properties of Cu-based Bulk Metallic Glass Composites
This work highlights the relationship between the preparation, crystallization behavior, microstructures, and mechanical properties of Cu-based bulk metallic glasses (BMGs) and their composites (BMGCs). (Cu47Zr45Al8)97.5Y1.5Nb in-situ BMGCs were prepared using isothermal annealing, and the experimental results indicate tunable mechanical properties of the al
Mat. Res.. Publicado em: 06/05/2019
-
18. Nb-doped Ti2O3 Films Deposited Through Grid-Assisted Magnetron Sputtering on Glass Substrate: Electrical and Optical Analysis
Abstract Niobium doped dititanium trioxide (Ti2O3:Nb) films were deposited on glass substrates, through grid-assisted magnetron sputtering. The Ti2O3:Nb films were characterized by X-ray diffraction (XRD), electrical conductivity and optical properties. Film deposition was carried out in two different substrate bias modes: DC and unipolar pulsed. Results sho
Mat. Res.. Publicado em: 24/01/2019
-
19. Microstructure and Mechanical Properties of AA6061/AZ31B/AA6061 Composite Plates Fabricated by Vertical Explosive Welding and Subsequent Hot Rolling
In this study, three-ply Al/Mg/Al composite plates were successfully achieved by vertical explosive welding (EXW) method. After EXW, the sound joints were obtained. Then thin three-ply Al/Mg/Al EXWed composite plates with the thickness of 1.78 mm were achieved by hot rolling. The influence of annealing on the interface microstructures and mechanical properti
Mat. Res.. Publicado em: 04/10/2018
-
20. Analysis of the Crystallographic Microtexture of a UNS S32205 and a UNS S32304 Duplex Stainless Steels After Cold Rolling and Heat Treatment
Samples of duplex stainless steel 32205 (standard duplex) and 32304 (lean duplex) were investigated in the as-received state, cold rolling (with thickness reduction of 64 % and 62 % respectively) and after annealing at 1055ºC for 20 s soaking. Crystallographic microtexture was obtained via Electron BackScatter Diffraction (EBSD) technique. The results showe
Mat. Res.. Publicado em: 26/07/2018
-
21. Effect of thermal treatment on points defects of Al-N codoped ZnO films
ABSTRACT The effect of annealing temperature on the structural properties of Al-N codoped ZnO films were studied by X-ray diffraction, photoluminescence and Raman spectroscopy. ZnO films were deposited by sputtering technique on silicon substrates at 20 ºC, Al-concentration was kept constant and N-flow was changed to 6, 12 and 15 sccm. A thermal treatment w
Matéria (Rio J.). Publicado em: 19/07/2018
-
22. Evolution of magnetic response as a function of annealing temperature in Fe-based alloys
ABSTRACT The magnetic response, coercive force and magnetic induction, in Fe-10at.% Si, Fe-6at.% Al-9at.% Si and Fe-4at.% Al-8at.% Ge alloys as a function of the annealing temperature was determined and correlated to the microstructural state. The microstructural characterization was made through differential thermal analysis, mechanical spectroscopy and neu
Matéria (Rio J.). Publicado em: 19/07/2018
-
23. Synthesis and characterization of nanostructured TiO2 and TiO2/W thin films deposited by co-sputtering
ABSTRACT Nanostructured TiO2 and TiO2/W thin films were deposited on Corning glass substrates by RF and DC magnetron co-sputtering at room temperature, using three targets of TiO, Ti and W. After deposition, samples were subjected to an annealing treatment in air at 500 °C for 3 hrs. The effect of the annealing treatment and tungsten addition to the TiO2 ma
Matéria (Rio J.). Publicado em: 19/07/2018
-
24. Identificación de precipitados en aleaciones U-Nb-Zr tratadas térmicamente a 850 ºC
ABSTRACT At the present, the international goal is to develop and qualify a very high U density fuel for high flux research reactors. The selected U-alloy must present an isotropic crystalline structure at the end of the fuel fabrication process. These types of structures exhibit stable behavior under irradiation. In particular, it is wanted to retain as met
Matéria (Rio J.). Publicado em: 19/07/2018