25. Influencia de sistemas adesivos sobre a resistencia a tração da união amalgama de prata-cimento de ionomero de vidro
The purpose of this study was to evaluate in vitro, the bond strengths of amalgam to glass ionomer cement, under the influence of adhesive systems. Specimens with distinct dimensions were used to each material in a manufactored cylindric Teflon matrix, with a conic-retentive central cavity. The glass ionomer used as base was the VIDRION F glass ionomer cemen
Publicado em: 1993
-
26. Estudo "in vitro" da rugosidade superficial de materiais restauradores submetidos a ensaio de escovação
The purpose of this study was to evaluate the surface roughness oí direct restorative materiaIs (composite resins, glass ionomers and amalgam) submitted to a in vitro toothbrushing test. Three composite resins (Herculite XR, Prisma APH and P50), two glass ionomers (Vidrion R and Chelon Fil) and an amalgam (Dispersalloy) were studied. Eigth samples of each m
Publicado em: 1993
-
27. Avaliação "In Vitro" da influencia do cimento adesivo panavia-ex, na infiltração marginal de restaurações de amalgama de prata
O objetivo deste trabalho foi avaliar "in vitro" a inflitração marginal de restaurações de amalgama em cavidades forradas com o adesivo Panavia EX e submetidas ou não ao condicionamento acido do esmalte cavo-superficial. Foram utilizados trinta dentes humanos recem-extraidos, entre os grupos de caninos e pré-molares que receberam preparos cavitarios de
Publicado em: 1991
-
28. Dureza superficial do amalgama : influencia dos operadores
Não informado
Publicado em: 1988
-
29. Liberação de cobre, estanho e mercurio de amalgamas dentais em saliva articial
The objective of the presente work was to determine the release of copper, tin and mercury from three dental amalgams, free from zinc, being one conventional and the others two with high contents of copper. Cornrnercially these arnalgams are avai1able as Standalloy F, Ventura III and Aristalloy 21 respectively. Seventy five test samples were prepared and inr
Publicado em: 1988
-
30. Estudo da adaptação marginal de amalgamas de prata sob a influencia de ligas, triturações e brunidura
The purpose of this work was to verify thesu! face adaptation of the lateral wall of silver amalgam specimens. The specimens were developed through three different silver alloys, whDse commercial names were: Novo True Dental loy, Navaloy and Sybraloy. These alloys were triturated mechanically or manually according to American Dental Association specification
Publicado em: 1985
-
31. Efeitos das variaveis brunidura , ciclo termico e periodos de armazenagem na infiltração marginal das restaurações de amalgama de prata
O objetivo deste estudo foi verificar os níveis de micro-infiltração marginal das restaurações confeccionadas com: limalha de prata de partículas (Novo True Dentalloy - SSWhite); de partículas convencionais com alto conteúdo de cobre (Novaloy - Sybron-Kerr) e de partículas esféricas com alto conteúdo de cobre (Sybraloy - Sybron-Kerr), nas seguinte
Publicado em: 1985