Eutectic Silicon
Mostrando 1-7 de 7 artigos, teses e dissertações.
-
1. Tensile and fatigue properties, machinability and machined surface roughness of Al-Si-Cu alloys
ABSTRACT In this paper, the aim was to determine if ASC91 (9 % Al, 1 % Cu) could be replaced with ASC73 (7 % Al, 3 % Cu) aluminium alloy, with presumably improved machinability due to lower silicon content (9 to 7 %) and retained mechanical properties due to a higher copper content (1 to 3 %). The test samples were excised from cylinder heads produced by the
Matéria (Rio J.). Publicado em: 16/09/2019
-
2. Evolución microestructural durante el envejecimiento a alta temperatura de una aleación 35Ni-25Cr-Nb
ABSTRACT The dendritic-type microstructure of the 35Ni-25Cr-Nb alloy, in the as-cast condition, consists of an austenitic matrix and two types of eutectic primary carbides; Nb-rich MC type and Cr-rich M23C6 type both presents in interdendritic edges and grain boundaries. During aging at 800ºC for different times, M23C6 type secondary carbides precipitate in
Matéria (Rio J.). Publicado em: 19/07/2018
-
3. Properties of SiC Ceramics Sintered via Liquid Phase Using Al2O3 + Y2O3, Al2O3 + Yb2O3 and Al2O3 + Dy2O3 as Additives: a Comparative Study
Silicon carbide (SiC) ceramics show excellent performance at high temperatures. Due to the high covalence of Si-C bonds, these ceramics are produced successfully only via liquid phase sintering (LPS). In this work, SiC ceramics were sintered via LPS using eutectic mixtures of Al2O3+Y2O3, which served as a standard for comparison, Al2O3+Yb2O3 and Al2O3+Dy2O3.
Mat. Res.. Publicado em: 2015-06
-
4. Efeito da modificação com estrôncio na microestrutura e nas propriedades mecânicas da liga 356 / Effect of strontium on the microstructure and mechanical properties alloys 356
The properties of aluminum-silicon alloys are strongly dependent on the casting process used, the chemical additions made to control eutectic structure, primary silicon and grain structure, and molten metal treatment to reduce hydrogen gas content and to remove inclusions. Modification treatments transform the flake eutectic silicon into a fibrous form produ
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 29/02/2012
-
5. Microstructural characterization of as-cast hf-b alloys
An accurate knowledge of several metal-boron phase diagrams is important to evaluation of higher order systems such as metal-silicon-boron ternaries. The refinement and reassessment of phase diagram data is a continuous work, thus the reevaluation of metal-boron systems provides the possibility to confirm previous data from an investigation using higher puri
Materials Research. Publicado em: 14/02/2012
-
6. Nucleation and growth of austenite/VC eutectic in alloys of the Fe-V-C system. / Nucleação e crescimento do eutético austenita/VC em ligas do sistema Fe-V-C.
The three most commercially important families of alloys for the foundry industry show the formation of faceted/non-faceted eutectics type during solidification: cast irons with graphite (austenite/graphite eutectic), white cast irons (austenite/carbide eutectic) and Al-Si alloys (alfa/silicon eutectic). In the case of white cast irons, the eutectic carbide
Publicado em: 2008
-
7. Influencia da espessura de parede de molde no tempo de solidificação e na estrutura de fundição da liga eutetica aluminmio-12% silicio (Silumin) / Influence of the mould wall thickeness on the solidification time and as-cast strucuture of commercial eutectic aluminum-12% silicon
O presente trabalho visa, essencialmente, analisar a influência do dimensionamento da espessura de parede de molde no tempo de solidificação e na estrutura final de peças fundi das em liga Alumínio-l2% Silício (Silumin), liga esta de larga utilização prática. Inicialmente faz-se uma revisão crítica. Os métodos existentes na literatura especializa
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 1977