1. Tailoring the properties of Y2O3 via synthesis parameters varied during the PVA-assisted sol-gel route
Abstract The effect of synthesis parameters on the microstructural behavior and morphology during the yttrium oxide (Y2O3) formation is reported. Y2O3 crystals were produced by a modified sol-gel route assisted by polyvinyl alcohol solution varying the calcination temperature and solution pH. The crystalline phase formation was investigated using X-ray powde
Cerâmica. Publicado em: 2023
-
2. Study of rhombohedral tricalcium phosphate in hexagonal crystal structure family on the sample prepared by the sol-gel route and the effect of calcination temperature
Abstract The effect of the calcination temperature at 800 and 1000 °C on the stable formation of the tricalcium phosphate with rhombohedral structure in the system of the hexagonal crystal family was determined, while its precursor was made from limestone obtained from nature in the Lumajang district, Indonesia. The rhombohedral tricalcium phosphate samples
Cerâmica. Publicado em: 2023
-
3. Synthesis of delafossite CuCrO2 via solution combustion method and its acid functionalization for biodiesel production
Abstract CuCrO2 was synthesized by solution combustion synthesis (SCS) and applied as a heterogeneous catalyst to produce soybean biodiesel. The combustion reaction was carried out using urea as a fuel, and copper (II) and chromium (III) nitrates as precursors. After the powders’ obtention, these were calcined and functionalized in an acidic medium. The po
Cerâmica. Publicado em: 2023
-
4. Evaluation of the Structural Integrity of Layered Double Hydroxides and Mesoporous Silica During the Preparation of Heterostructures
Heterostructures constructed with mesoporous silica and layered double hydroxides are interesting for catalytic and drug delivery applications. Different arrangements between these phases are possible. In this study, we prepared heterostructures by embedding layered double hydroxides phases [M4Al2(OH)12](CO3) (M = Mg2+ or Zn2+) within the MCM41 mesoporous si
Journal of the Brazilian Chemical Society. Publicado em: 2022
-
5. Analysis and evaluation of structural properties of Co3O4 microparticles obtained at low temperature
Abstract In the present research, the synthesis of cobalt oxide Co3O4 was carried out using the sol-gel technique with subsequent heat treatment at 225 and 235 °C. The final product obtained was characterized by X-ray diffraction (XRD), showing a pure crystalline phase of Co3O4, cell parameters a=b=c=8.071 Å, and a volume of 525.7 Å3. The particle size wa
Cerâmica. Publicado em: 2022
-
6. K2O SUPORTADO EM ZEÓLITA NATURAL: SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO PRODUÇÃO DE BIODIESEL A PARTIR DO ÓLEO DE GIRASSOL
Biodiesel is a renewable fuel, a substitute for fossil diesel, which is important for reducing GHG in Brazil. Therefore, this work aims to synthesize and characterize the catalyst using the support of natural zeolite impregnated with K2O and apply it in the production of biodiesel through the transesterification reaction. Through the analysis of characteriza
Química Nova. Publicado em: 2022
-
7. EFFECT OF REACTION CONDITIONS ON PARTICLE SIZE OF ZNO NANOPARTICLES VIA CONTROLLED PRECIPITATION METHOD AND IN-VITRO ANTIBACTERIAL CAPACITY
High-yield ZnO spheroidal nanoparticles with an average diameter around 23 nm (≈ 25% frequency) and 30 nm (≈ 28% frequency) were obtained by controlled semicontinuous precipitation at low temperatures. This synthesis was obtained from hydrozincite (Zn5(CO3)2(OH)6) as primary nanoparticles. The Zn5(CO3)2(OH)6 nanoparticles were synthesized by hydrolysis o
Química Nova. Publicado em: 2022
-
8. Thermal, structural and optical properties of magnetic BiFeO3 micron-particles synthesized by coprecipitation method: heterogeneous photocatalysis study under white LED irradiation
Abstract Bismuth ferrite, BiFeO3 (BFO) prepared via a coprecipitation method, was used as an effective photocatalyst for the degradation of methylene blue (MB) using a white light-emitting diode (LED-50 W) lamp. The as-prepared material was characterized by TGA, XRD, SEM-EDX, FTIR, and UV-vis-DRS techniques. The effects of experimental key parameters such as
Cerâmica. Publicado em: 2022
-
9. Characterization and mechanical properties of one-part geopolymer based on a pure metakaolin
Abstract Geopolymers are amorphous silicate polymers that have been extensively studied due to their applications, scientific and technical relevance, and their potential as cement in substitution to Portland. Much of the focus has been in the use of precursors and aggregates that are rarely pure and homogeneous with the use of tailings being very common. Th
REM - International Engineering Journal. Publicado em: 2022
-
10. Effect of pH level and calcination on the production of calcium phosphates by acidic route of wet precipitation
Abstract Multiphasic calcium phosphate powders were synthesized by the acidic route, using lactic acid as a chelating agent that allows the production of a stable and rich solution of calcium and phosphate ions at room temperature. After pH adjusting, without varying the concentrations of precursor solution, XRD and FTIR analyses showed different CaP phases
Cerâmica. Publicado em: 2021-06
-
11. Evaluation of the properties of a foamed geopolymer developed with different types of metakaolin
Abstract The physical and mechanical properties of foamed geopolymers were determined. The geopolymers were made with two different metakaolins (from Metacaulim do Brasil - MB, and Pantano Grande/RS - MPG) as precursors, with NaOH and Na2SiO3 as activators, and with the addition of foam, which was produced with the foaming agent diethanolamide of coconut fat
Cerâmica. Publicado em: 2021-06
-
12. Study of structural, optical, and morphological characteristics of manganese titanate (MnTiO3) obtained by combustion reaction using microwave energy
Abstract MnTiO3 is a semiconductor that has relevant dielectric and optical properties. For the synthesis of manganese titanate (MnTiO3) powders, the combustion method via microwave and subsequent calcination at 500, 700, and 900 °C were used. The structural, morphological, and optical properties of the samples were investigated. X-ray diffraction analyzes
Cerâmica. Publicado em: 2021-03