Microestrutura e deformação a quente de um aço dinx20cr13 na laminação de tubos sem costura
AUTOR(ES)
Meire Guimaraes Lage
DATA DE PUBLICAÇÃO
2008
RESUMO
The DIN X20Cr13 stainless steel is a high technological alloy usually used in oil industry for onshore and offshore tubing applications. In this study DIN X20Cr13 equilibrium diagrams were made by Thermo-Calc software to study transformation reactions in solid state phases. This stainless steel was submitted to different heat treatments in order to generate delta ferrite to characterize and quantify it. Hot torsion tests were made to study DIN X20Cr13 mechanical properties and softening kinetic. The results showed that polygonal delta ferrite was not built with quantity enough to damage DIN X20Cr13 steel mechanical properties during the rolling process seamless steel tubes. The ferrite originated from the decarburized austenite could be related to the damage on DIN X20Cr13 mechanical properties by promoting wrinkles in seamless steel tubes. The hot deformation equation and the peak stress equation for DIN X20Cr13 could be described in this study
ASSUNTO(S)
engenharia de minas teses. laminação (metalurgia) teses. ciencia dos materiais teses. engenharia metalúrgica teses.
ACESSO AO ARTIGO
http://hdl.handle.net/1843/MAPO-7QJQAZDocumentos Relacionados
- Envelhecimento por Deformação em Juntas Soldadas de Tubos de Aço API5L X65Q sem Costura
- Estudo das características microestruturais e propriedades mecânicas em tubos de aço com costura normalizados
- Influência da deformação na laminação de encruamento nas propriedades mecânicas do aço acalmado ao alumínio refosforado, galvanizado a quente classe 220mpa de limite de escoamento
- Simulação em laminador piloto da influência da lubrificação durante o processo de deformação a quente na microestrutura e textura do aço inoxidável ferrítico AISI 430
- Estudo da laminação a quente do aço rapido ABNT M2