Influencia de la cantidad de O2 adicionado al CO2 en el gas de protección sobre la microestructura del metal depositado en uniones soldadas de bordes rectos en aceros de bajo contenido de carbono con el proceso GMAW

AUTOR(ES)

Díaz-Cedré, Eduardo, Cruz-Crespo, Amado, Ramos Morales, Félix, Tello Rico, Mauricio, Chaparro Gonzáles, Joel, Rodríguez Pérez, Manuel, Pozo Morejón, Juan A, Pérez Pino, Nancy M.

FONTE

Soldagem & Inspeção

DATA DE PUBLICAÇÃO

2010-12

RESUMO

The presence of acicular ferrite (AF) in the microstructure of weld bead, in a specified range of values, increase considerably the toughness of welded joints. The present paper, for that reason, study the relationship between the acicular ferrite quantity in the deposited metal and the oxygen present in the active gas mixture of CO2+O2, during the execution of butt welded joints with straight edges, in low carbon steels with consumable electrode and gas protection (GMAW) in invariable conditions of process parameters (welding current, arc voltage, welding speed, electrode extension, and gas flow). The graphic relation between the acicular ferrite and the oxygen content was established, as result of the research work.

Documentos Relacionados

• Vida a fatiga de uniones soldadas mediante PAW de aceros microaleados al boro
• Estabilidad de la austenita retenida bajo condiciones de deformación en aceros multifásicos con bainita nanoestructurada
• Evolución Microestructural en Uniones de la Aleación Ti-6Al-4V Mediante el Proceso de Soldadura de Punto por Fricción-agitación
• Efecto de la Composición Química del Metal de Aporte y del Calor Aportado Sobre la Microestructura y las Propiedades Mecánicas de Juntas Soldadas de Aceros Inoxidables Dúplex
• Empleo de explosivos en el alivio de tensiones residuales de la zona de influencia térmica de uniones soldadas