Influencia da geometria da junção soldada na resistencia a fadiga de ligas do sistema cobalto-cromo
AUTOR(ES)
Marcos Blanco Cargiani
DATA DE PUBLICAÇÃO
1998
RESUMO
The purpose of this study was to investigate the fatigue stength of the system Co-Cr (Dentorium and Degussa), submitted or not to the procedure conventional soldering. Cylindrical eighty specimens with 1,7 mm in diameter were casted utilizing oxi-acetilene torch for each alloys kind. The soldering procedure was realizated in sixty specimens of each alloy and twenty were control. the soldering were obtained by Co-Cr welding rods and gas-oxygen torch. the solder gap selected was 0.3 mm for each prepared (top to top, chamfer 30° and pencil point). The fatigue strength was conducted in a AMSLER (alfred J. Amsler &Co. - Shaffhausen Schaweis - Switzerland) fatig~e testing machine and the specimens were sujected to a tensile load of 1 kg, and a ciclic stress amplitude of 2°. After failure, the cycles were registered and the fracture surface was examined with (S.E.M.). The results were statistically analysed using a Mann-Whitney. The results of this study indicated that: 1 - For the Dentorium alloy the three types of prepare (with solder) presented- values of strength statistically similar to each other but inferior statistically than control (without solder); 2 - For the Degu ssa alloy, the type of prepared pencil point and top to top (with solder) showed the similar results statistically, but inferior statistically to the control (without solder) in chamfer of 30°. No statistical difference wás found between the control and prepared in chamfer of 30°; 3 - The Dentorium alloy presented resistance values of fatigue superior statistically the degussa alloy, when it solde r was made in prepare pencil point. No statistical difference was observed for the control and ty pes of prepared in chamfer 30° and top to topo
ASSUNTO(S)
metais - fadiga solda e soldagem ligas de metais de transição protese dentaria parcial removivel
ACESSO AO ARTIGO
http://libdigi.unicamp.br/document/?code=vtls000128974Documentos Relacionados
- Análise mecânica e microestrutural das ligas de cobalto-cromo de uso odontológico após sucessivas refundições
- Estudo eletroquímico de ligas à base de cobalto-cromo e níquel-cromo
- Influência de estrutura metálica de cobalto-cromo na rugosidade e dureza Knoop superficiais de resinas acrílicas polimerizadas por luz visível
- Stent coronário de liga cobalto-cromo concebido no Brasil: achados histológicos preliminares em modelo experimental porcino
- Permanent deformation in vitro study of I bar clasps cast with cobalt-chromium alloy and commercially pure Titanium, submitted to tension-deformation trials.