Estudo comparativo entre sílica obtida por lixívia ácida da casca de arroz e sílica obtida por tratamento térmico da cinza de casca de arroz
AUTOR(ES)
Della, Viviana Possamai, Hotza, Dachamir, Junkes, Janaína Accordi, Oliveira, Antonio Pedro Novaes de
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2006-12
RESUMO
A comparison between silica by acid leaching of rice husk (RH) and silica obtained from thermal treatment of rice husk ash (RHA) is presented. The best leaching results were obtained using 10% hydrochloric acid followed by washing with water. The alternative method, calcination of RHA at 700 ºC for 6 h followed by grinding for 80 min, was more effective. Silica obtained from RH was about 97% amorphous, had a 17.37 µm mean particle size, and a specific surface area of 296 m²/g. On the other hand, for silica obtained from RHA the values were about 95% amorphous material 0.68 µm, and 81 m²/g.
Documentos Relacionados
- Síntese e caracterização de mulita utilizando sílica obtida da casca de arroz
- Caracterização de cinza obtida por combustão de casca de arroz em reator de leito fluidizado
- Biotransformação da cinza da casca de arroz em nanopartículas de sílica mediante Fusarium oxysporum
- Produção de geopolímeros utilizando cinza da casca de arroz como fonte complementar de sílica
- Emprego da cinza da casca de arroz como única fonte de sílica na formação de materiais mesoporosos