Efeito da ativação mecânica de uma formulação de talco/caulim/alumina sobre o mecanismo e a cinética de formação de cordierita

AUTOR(ES)

Rodrigues Neto, João Batista, Hotza, Dachamir, Moreno, Rodrigo

FONTE

Quím. Nova

DATA DE PUBLICAÇÃO

2014-04

RESUMO

In this study, the influence of mechanical activation by intensive ball milling of a stoichiometric mixture of talc, kaolin, and alumina on the mechanism and kinetics of cordierite (2MgO·2Al2O3·5SiO2) formation was evaluated. The raw materials were characterized by chemical analysis, X-ray diffraction (XRD), laser diffraction, and helium pycnometry. The kinetics and mechanism of cordierite formation were studied by XRD, differential thermal analysis, and dilatometry in order to describe the phase formation as a function of temperature (1000-1400 ºC), time of thermochemical treatment (0-4 h), and grinding time of the mixture (0-45 min). Finally, the optimal conditions of the thermochemical treatment that ensured the formation of cordierite were determined: milling time of 45 min and thermal treatment at 1280 ºC for 1 h.

Documentos Relacionados

• Oxidação de propeno em catalisadores de CuO suportados em CeO2/y-alumina/cordierita
• Efeito da ventilacao natural e mecanica sobre o desempenho de porcas em lactacao.
• Efeito das técnicas de inserção e ativação da resina composta sobre a microinfiltração e microdureza
• Efeito da aplicação de vibração mecânica sobre a impulsão vertical
• Evaluacion termica, mecanica y electrica de materiales compuestos cordierita-mullita